410 Stainless Steel Bar
410 is the basic, general purpose, hardenable martensitic stainless steel. It is used for highly stressed parts with good corrosion resistance and strength.
Also referred to as “general purpose grade steel”, this can be hardened to various strengths and to improve its corrosion resistance. 410 is best suited for applications that require mild corrosion resistance, heat resistance, and high strength. Typically used in aerospace structures, automotive exhausts, manifolds, and high-temperature engine components, medical instruments and devices, petrochemical applications, and cutlery.
Product Description
| Product | 410 Stainless Steel Bar |
| Standard | AMS 5504, ASME SA240, ASTM A240 |
| Shape | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, HRAP, Bright, Forging Etc. |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Outside Diameter | 4mm to 500mm |
| Length | 2 meters – 7.5 meters, or Custom Cut Lengths |
| MOQ | 1 Ton |
Corrosion Resistance:
Good corrosion resistance to atmospheric corrosion, potable water, and to mildly corrosive environments
Its exposure to everyday activities (sports, food preparation) is generally satisfactory when proper cleaning is performed after exposure to use
Good corrosion resistance to low concentrations of mild organic and mineral acids
Chemistry Information of 410 Stainless Steel Bar
| Element | C | Mn | Si | Cr | Ni | S | P |
| Percentage | 0.15 max | 1 max | 1 max | 11.5 – 13.5 | 0.75 max | 0.03 max | 0.04 max |
Physical Properties of 410 Stainless Steel Bar
| Density | 0.282 lb/in3 | |
| Ultimate Tensile Strength | 76 ksi | |
| Yield Tensile Strength | 42 ksi | |
| Shear Modulus | 11,000 ksi | |
| Shear Strength | 48 ksi | |
| Fatigue Strength | 28 ksi | |
| Hardness Rockwell | Brinell | B84 | 162 | |
| Elongation at Break Percentage | 22% | |
| Reduction of Area | 47% | |
| Modulus of Elasticity | 28,000 ksi | |
| Poisson’s Ratio | 0.28 | |
| Machinability Percentage | 54% | |
| Melting Point | 2,700-2,790 °F | |
| Specific Heat | 1.1 x 10^-1 BTU/lb-°F | |
| Thermal Conductivity | 204 BTU-in/hr-ft^2-°F | |
| Electrical Conductivity | 2.9% IACS |
Mechanical Properties:
| Grade | Tensile Strength ksi (MPa) min | Yield Strength 0.2% offset ksi (MPa) min | Elongation (% in 50mm) min | Hardness (Brinell) MAX | Hardness (Rockwell B) MAX |
| 410 | 65 (450) | 30 (205) | 20 | 217 | 96 |
Applications:
- Cutlery
- Steam and gas turbine blades
- Kitchen utensils
- Bolts, nuts, screws
- Pump and valve parts and shafts
- Mine ladder rugs
- Dental and surgical instruments
- Nozzles
- Hardened steel balls and seats for oil well pumps
Application
Agricultural Modernization
Construction Engineering
Environmental Protection Engineering
Food Processing Industry
Intelligent Home Appliances
Medical and Health Field
New Energy Infrastructure