5182 Aluminum Coil
5182 aluminum alloy is a wrought alloy type with good corrosion resistance. Weldability and resistance to corrosion of 5182 aluminum alloy is considered favorable. The following datasheet will provide more details about 5182 aluminum alloy. 5182 aluminium alloy has magnesium and manganese as minor elements. 5182 Aluminium alloy is used in the automobile industry for making various parts of vehicles.
The 5182 aluminum alloys are representative products of aluminum alloys with medium strength and good corrosion resistance and weldability. They are widely used in all fields from thin plates to thick plates. 5182 aluminum alloy belongs to the Al-Mg-Si series alloy and has a wide range of applications. Especially the construction industry cannot do without this alloy. It is the most promising alloy. Good corrosion resistance, excellent weldability, good cold workability, and medium strength. The main alloying element of 5182 is magnesium, which has good forming performance, corrosion resistance, weldability, and medium strength. It is used to manufacture aircraft fuel tanks, oil pipes, and sheet metal parts of vehicles and ships, meters, street lamp brackets and rivets, Hardware products, electrical enclosures, etc.
Product Description
| Product | 5182 |
| Temper | O,H12,H14,H16H18,H19,H22,H24,H26,H28,H32,H34,H36,H38 |
| Thickness（mm） | 0.2-8.0 |
| Gauges (Thickness) | 0.1mm – 4.0mm (tight tolerances to 1/4 commercial) Additional: 4mm – 8.255mm (subject to inquiry) |
| Widths | 6.0mm – 940mm (tight tolerances) Additional: 19mm – 1879mm (subject to inquiry) |
| Inside Diameters | 152.4mm, 203.2mm, 254.0mm, 304.8mm, 406.4mm, 508.0mm, 609.6mm (cores available) |
| Outside Diameter | Maximum 1981mm |
| Coil Weight | Up to 7.9 kg per mm of width |
| Applications | Deep drawing, anodizing, minimum earring, fine-grain applications |
| Surface Finishes | – Z-Mill Standard: 0.07-0.15μm Ra (brighter than conventional 4-Hi) – Matte: 0.3-0.4μm Ra – Bright (1 or 2 sides): 0.025-0.05μm Ra – Custom surfaces are available upon inquiry |
| Special Processing | Leveling, cut-to-length, cleaning (inquire for details) |
| Coatings | Oiling, anodizing, painting, strippable plastic coating (inquire for details) |
| Packaging | Custom packaging to meet requirements Export packaging compliant with the IPPC International Standards |
Chemical Composition of 5182 Aluminum Coil
| Si Silicon |
Fe Iron |
Cu Copper |
Mn Manganese |
Mg Magnesium |
Cr Chromium |
Ni Nickel |
Zn Zinc |
Ti Titanium |
Others Each |
Total |
Total Aluminum Min |
| 0.2 | 0.35 | 0.15 | 0.2 – 0.5 | 4.0 – 5.0 | 0.1 | – | 0.25 | 0.1 | 0.05 | 0.15 | Remainder |
Mechanical Properties of 5182 Aluminum Coil
| Properties | Metric | Imperial |
| Tensile strength | 275 MPa | 39900 psi |
| Yield strength | 130 MPa | 18900 psi |
| Elongation at break (@thickness 1.60 mm/0.0630 in) | 21% | 21% |
| Elastic modulus | 69.6 GPa | 10100 ksi |
| Shear modulus | 26 GPa | 3770 ksi |
| Poisson’s ratio | 0.33 | 0.33 |
| Hardness, Brinell | 74 | 74 |
| Hardness, Knoop (converted from Brinell hardness value) | 97 | 97 |
| Hardness, Vickers (converted from Brinell hardness value) | 84 | 84 |
Thermal Properties of 5182 Aluminum Coil
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Thermal conductivity | 123 W/mK | 25 | All |
Application
Agricultural Modernization
Construction Engineering
Environmental Protection Engineering
Food Processing Industry
Intelligent Home Appliances
Medical and Health Field
New Energy Infrastructure